Products Description
Our expanded graphite materials—including flexible sheets, foil, paper, tape, and strips—are manufactured using a proprietary exfoliation process. Natural graphite flakes undergo chemical intercalation and high - temperature expansion (forming worm - like structures with 0.003g/cc density), then are rolled into binder - free coils. This vertically integrated production chain ensures consistent quality and rapid order fulfillment.
-
Automated Manufacturing
- 24/7 operation of CNC rolling mills producing 800+ meters of coils daily
- Laser cutting systems processing 1500+ gasket shapes per hour
-
Global Inventory Network
- 10,000+ m² warehouse with 500+ tons of stock in:
- China (main facility)
- Rotterdam (EU distribution hub)
- Houston (US inventory center)
-
Expedited Logistics
- DHL/FedEx partnerships for 3 - 5 day delivery to 90+ countries
- Customized packaging for air/sea/rail transport
- Purity: 99.8%+ carbon content (ICP - AES tested)
- Temperature Range: - 200°C to +1600°C
- Density Options: 0.8–1.25g/cm³ (stocked in 0.1g/cm³ increments)
- Stock Sizes:
- Coils: 1000mm/1500mm width, 30m/50m/80m length
- Sheets: 1000mm x 1500mm, thicknesses 0.15mm–5mm
- Customization:
- Non - standard sizes available within 48 hours
- Composite materials (graphite + metal/PTFE) ready in 7 days
- ISO 9001:2015 certified production
- In - line testing for:
- Compressive strength (ASTM F36)
- Thermal conductivity (ASTM C518)
- Gas tightness (ASTM F137)
A German chemical plant received 12,000 custom - cut gaskets within 72 hours via our Rotterdam hub, avoiding $2M in downtime costs.
- Speed: Average lead time 3–10 days (30% faster than industry average)
- Reliability: 99.6% on - time delivery record tracked via blockchain
- Cost - Effective: No premium charges for expedited orders over 500kg
Order Now
- Instant online quotes
- Free samples dispatched within 24 hours
- Dedicated account manager for urgent requirements
Your mission - critical sealing needs, delivered at light speed.
| Item | Standard Value |
| C concentration | 99% |
| S concentration | <1000ppm |
| chlorine concentration | <45ppm |
| tensile strength | 4.5MPa |
| compressibility | >40% |
| recovery | >10% |
| Temperature | -200ºC-600ºC |
| Pressure | 20MPa |
| Terence of Thickness | -0.04mm~+0.04mm |
| Terence of Dimension | In accordance with your Gasket size |
| Terence of Density | -0.06~g/cm3+0.06gcm3 |
Grades Separate :JB/T53392-1999 | Mechanical Data | Qualified product | Top Grade | Superior Grade |
Density Tolerance
g/cm3 | <0.4 | ±0.10 |
±0.05 |
| ≥0.4 | ±0.07 |
| Tensile Strength MPa | ≥3.2 | ≥4.5 | ≥5.0 |
| Compression Ratio % | 35~55 |
| Rebound Rate % | ≥9 | ≥11 | ≥12 |
| Stress relaxation rate % | ≤10 |
| Ash % | ≤6.0 | ≤3.0 | ≤1.0 |
| Heat loss on ignation % | 450ºC | ≤1.0 | ≤0.5 |
| 600ºC | ≤20 | ≤15 |
Sulphur content | ≤1500ppm | ≤1000ppm | ≤600ppm |
Chloride content | ≤100ppm | ≤50ppm | ≤20ppm |
| | | | | |